The invention discloses a temperature-resistant additive for rubber, which consists of the following substances: aluminium hydroxide, nano-alumina, nano-titanium dioxide, silica, stearic acid, glass fiber, aluminate coupling agent, sodium hexametaphosphate, attapulgite and liquid paraffin. The invention rationally matches a variety of raw material ingredients, among which aluminium hydroxide, nano-alumina, nano-titanium dioxide, silica and glass fiber are added and used to form a complex and dense network structure in rubber, which improves the stability of rubber molecular chain, enhances its temperature resistance, insulation and mechanical quality characteristics, and obviously improves the service performance of rubber. It has great market competitiveness and popularization value.
【技術實現步驟摘要】
一種橡膠用耐溫添加劑
本專利技術屬于橡膠加工處理
，具體涉及一種橡膠用耐溫添加劑。
技術介紹
橡膠（Rubber）是指具有可逆形變的高彈性聚合物材料，在室溫下富有彈性，在很小的外力作用下能產生較大形變，除去外力后能恢復原狀。橡膠屬于完全無定型聚合物，它的玻璃化轉變溫度（Tg）低，分子量往往很大，大于幾十萬。早期的橡膠是取自橡膠樹、橡膠草等植物的膠乳，加工后制成的具有彈性、絕緣性、不透水和空氣的材料。高彈性的高分子化合物?，F有的橡膠在耐溫、絕緣特性上還需進一步的提升。
技術實現思路
本專利技術的目的是針對現有的問題，提供了一種橡膠用耐溫添加劑。本專利技術是通過以下技術方案實現的：一種橡膠用耐溫添加劑，由如下重量份的物質組成：10~15份氫氧化鋁、30~35份納米氧化鋁、8~12份納米二氧化鈦、10~14份白炭黑、2~4份硬脂酸、6~9份玻璃纖維、3~5份鋁酸酯偶聯劑、1~3份六偏磷酸鈉、5~8份凹凸棒土、1~2份液體石蠟。優選的，由如下重量份的物質組成：13份氫氧化鋁、32份納米氧化鋁、10份納米二氧化鈦、12份白炭黑、3份硬脂酸、8份玻璃纖維、4份鋁酸酯偶聯劑、2份六偏磷酸鈉、7份凹凸棒土、1.5份液體石蠟。進一步的，所述的納米氧化鋁和納米二氧化鈦的顆粒粒徑均為20~50nm。進一步的，所述的氫氧化鋁和白炭黑的顆粒粒徑均為1~15μm。進一步的，所述的凹凸棒土的顆粒粒徑為50~100μm。本專利技術相比現有技術具有以下優點：本專利技術合理搭配了多種原料成分，其中氫氧化鋁、納米氧化鋁、納米二氧化鈦、白炭黑配合玻璃纖維的添加使用，在橡膠內形成了一復雜致密的網...
【技術保護點】
1.一種橡膠用耐溫添加劑，其特征在于，由如下重量份的物質組成：10~15份氫氧化鋁、30~35份納米氧化鋁、8~12份納米二氧化鈦、10~14份白炭黑、2~4份硬脂酸、6~9份玻璃纖維、3~5份鋁酸酯偶聯劑、1~3份六偏磷酸鈉、5~8份凹凸棒土、1~2份液體石蠟。
【技術特征摘要】
1.一種橡膠用耐溫添加劑，其特征在于，由如下重量份的物質組成：10~15份氫氧化鋁、30~35份納米氧化鋁、8~12份納米二氧化鈦、10~14份白炭黑、2~4份硬脂酸、6~9份玻璃纖維、3~5份鋁酸酯偶聯劑、1~3份六偏磷酸鈉、5~8份凹凸棒土、1~2份液體石蠟。2.根據權利要求1所述的一種橡膠用耐溫添加劑，其特征在于，由如下重量份的物質組成：13份氫氧化鋁、32份納米氧化鋁、10份納米二氧化鈦、12份白炭黑、3份硬脂...