The invention discloses a wood plastic PVC foamboard, comprising the following components: PVC 50 100; calcium powder 30 80; AC yellow foaming agent 0.2 0.5; ACyellow foaming agent 0.2 0.5; NC white foaming agent 1 1.5; NCwhite foaming agent 1 1 1 1 1 1.1.5; foaming regulator 5 10; stabilizer 3 8209 5; plasticizer 0.1 8209 plasticizer 0.1 8209 0.5; plasticizer 0.1 anti-impact modifier 1 8209; 5; internal lubricant 0.5 8209 9; internal lubricant 0 5 lubricant 0.5 8209 9; external lubricant 0.5 By weight. Plan. The invention adds wood flour to the formula of PVC foam board to make the produced wood-plastic PVC foam board have high hardness, high strength, good thermoplasticity and high cost performance. It not only meets the market demand, but also reduces the cost.
【技術實現步驟摘要】
一種木塑PVC發泡板
本專利技術涉及一種發泡板，具體涉及一種木塑PVC發泡板。
技術介紹
PVC發泡板又稱為雪弗板和安迪板，其化學成分是聚氯乙烯，和傳統木質材料相比，具有以下優點：防水、阻燃、耐酸堿、防蛀、質輕、保溫、隔音、易加工、可塑性強，因此被廣泛用于加裝建筑裝修材料，市場需求量很大。但目前市場上，PVC發泡板具有硬度和強度低、易損壞、使用年限較短等不足。
技術實現思路
專利技術目的：本專利技術目的在于針對現有技術的不足，提供一種硬度大、強度大、熱塑性好、性價比高的木塑PVC發泡板。技術方案：本專利技術所述的木塑PVC發泡板，包括如下組分：SG-5型聚氯乙烯50-100份；鈣粉30-80份；AC黃發泡劑0.2-0.5份；NC白發泡劑1-1.5份；發泡調節劑5-10份；穩定劑3-5份；增塑劑0.1-0.5份；抗沖擊改性劑1-5份；內潤滑劑0.5-1份；外潤滑劑0.5-2份；木粉20-40份；以重量份數計。優選地，所述的木塑PVC發泡板，包括如下組分：SG-5型聚氯乙烯75份；鈣粉50份；AC黃發泡劑0.4份；NC白發泡劑1.1份；發泡調節劑7.5份；穩定劑3.4份；增塑劑0.25份；抗沖擊改性劑2份；內潤滑劑0.7份；外潤滑劑0.9份；木粉25份；以重量份數計。優選地，所述的木塑PVC發泡板，包括如下組分：SG-5型聚氯乙烯75份；鈣粉50份；AC黃發泡劑0.3份；NC白發泡劑1.1份；發泡調節劑8份；穩定劑3.6份；增塑劑0.28份；抗沖擊改性劑3份；內潤滑劑0.8份；外潤滑劑0.8份；木粉28份；以重量份數計。有益效果：本專利技術通過在PVC發泡板配方中...
【技術保護點】
1.一種木塑PVC發泡板，其特征在于，包括如下組分：聚氯乙烯50?100份；鈣粉30?80份；AC黃發泡劑0.2?0.5份；NC白發泡劑1?1.5份；發泡調節劑5?10份；穩定劑3?5份；增塑劑0.1?0.5份；抗沖擊改性劑1?5份；內潤滑劑0.5?1份；外潤滑劑0.5?2份；木粉20?40份；以重量份數計。
【技術特征摘要】
1.一種木塑PVC發泡板，其特征在于，包括如下組分：聚氯乙烯50-100份；鈣粉30-80份；AC黃發泡劑0.2-0.5份；NC白發泡劑1-1.5份；發泡調節劑5-10份；穩定劑3-5份；增塑劑0.1-0.5份；抗沖擊改性劑1-5份；內潤滑劑0.5-1份；外潤滑劑0.5-2份；木粉20-40份；以重量份數計。2.根據權利要求1所述的木塑PVC發泡板，其特征在于，包括如下組分：聚氯乙烯75份；鈣粉50份；AC黃發泡劑0.4份...