The invention discloses a nano-composite hydrogen storage material, whose chemical formula is Mg/Mg1.2Zn0.3La0.5Ni, in which the content of Mg is 5-10wt%. The invention also discloses a method for preparing nano-composite hydrogen storage materials, which includes the following steps: 1) preparing Mg1.2Zn0.3La0.5Ni alloy by solid phase diffusion after mixing Mg1.2Zn0.3La0.5Ni powder with zinc powder, lanthanum powder and nickel powder according to the stoichiometric ratio of Mg1.2Zn0.3La0.5Ni; 2) mixing Mg1.2Zn0.3La0.5Ni alloy prepared by step 1 with magnesium powder, and placing it in planetary ball mill under inert gas protection for 500-800 years. The nano-composite hydrogen storage material is obtained by ball milling for 12-48 hours in r/min. The nano-composite hydrogen storage material is prepared by a simple and low-cost method, and the nano-composite hydrogen storage material has good hydrogen absorption kinetics performance.
【技術實現步驟摘要】
一種納米復合儲氫材料及制備方法
本專利技術屬于儲氫材料
，具體涉及一種納米復合儲氫材料Mg/Mg1.2Zn0.3La0.5Ni及制備方法。
技術介紹
氫氧燃料電池氫能利用率高，清潔無污染，近年已成為電動汽車電池的研究熱點。從安全角度和成本角度考慮，金屬氫化物是理想的氫源材料。鎂儲氫量高、儲量豐富，被認為是最有前途的儲氫材料。然而，鎂吸放氫熱力學和動力學性能較差，因此限制了其作為儲氫材料的應用。鎂與其它儲氫合金的復合是改善鎂吸放氫性能的有效方法。
技術實現思路
專利技術目的：本專利技術的目的是提供一種具有較好的吸放氫性能的鎂基儲氫材料技術。技術方案：本專利技術提供一種納米復合儲氫材料，其化學式為Mg/Mg1.2Zn0.3La0.5Ni，其中Mg含量為5~10wt%。本專利技術另一方面提供一種制備納米復合儲氫材料的方法，該方法包括以下步驟：1）將鎂粉、鋅粉、鑭粉和鎳粉按照Mg1.2Zn0.3La0.5Ni化學計量比混合后通過固相擴散法制備Mg1.2Zn0.3La0.5Ni合金；2）將步驟1）制得的Mg1.2Zn0.3La0.5Ni合金與鎂粉混合，惰性氣體保護下置于行星球磨機中500~800r/min球磨12~48小時，即得到所述納米復合儲氫材料。優選地，惰性氣體為氮氣或氬氣。有益效果：本專利技術通過簡單、低成本的方法制得了納米復合儲氫材料Mg/Mg1.2Zn0.3La0.5Ni，該納米復合儲氫材料具有良好的吸氫動力學性能。具體實施方式實施例1一種納米復合儲氫材料，其化學式為Mg/Mg1.2Zn0.3La0.5Ni，其中Mg含量為5wt%。其制備方法包括以下步...
【技術保護點】
1.一種納米復合儲氫材料，其特征在于，該納米復合儲氫材料化學式為Mg/Mg1.2Zn0.3La0.5Ni。
【技術特征摘要】
1.一種納米復合儲氫材料，其特征在于，該納米復合儲氫材料化學式為Mg/Mg1.2Zn0.3La0.5Ni。2.根據權利要求1所述的納米復合儲氫材料，其特征在于，Mg/Mg1.2Zn0.3La0.5Ni中Mg含量為5~10wt%。3.一種制備權利要求1所述的納米復合儲氫材料的方法，其特征在于，該方法包括以下步驟：1）將鎂粉、鋅粉、鑭粉和鎳粉按照Mg1.2...