The invention discloses a preparation method of capacitor with high crystallinity of biaxially oriented polypropylene film capacitor, the characteristics of the isotacticity of more than 98%, ash content is less than 15ppm, 2.0g/10min ~ 3.2g/10min melt index polypropylene resin material, the temperature and cooling rate and stress for high temperature resistant polypropylene film capacitor with high crystallinity the capacitance by the thin film prepared by the invention has light weight, low loss, good stability, excellent electrical insulation characteristics and mechanical properties, have high temperature performance, the capacitor with this film made in the run in 110 DEG C for a long time in bad environment.
【技術實現步驟摘要】
電容器用高結晶度雙向拉伸聚丙烯電容膜的研制方法
本專利技術屬于僅用碳-碳不飽和鍵反應得到的高分子化合物的制備方法，涉及一種電容器用高結晶度雙向拉伸聚丙烯電容膜的制造方法，制得的電容器可在110℃的惡劣環境下長期運行。
技術介紹
現有的聚丙烯電容薄膜，由于其內部微觀結構等原因，由于橫向收縮率相對偏大，在金屬化電容器制作與使用過程中，易造成的缺陷有：兩端金屬層與薄膜表面金屬度層連接不好，引起介質損耗角正切增大，電容器溫度升高，使電容器易擊穿，且由于橫向收縮嚴重，造成電容器容量下降，同時現有電容膜的耐壓性能相對偏低，拉伸強度偏小，耐溫性能差。
技術實現思路
針對上述情況，本專利技術的目的在于提供一種熱穩定性好、耐高溫、拉伸強度大的高結晶度雙向拉伸聚丙烯電容膜及其生產方法。本專利技術得到的高結晶度聚丙烯電容薄膜，120℃下靜置15分鐘時的橫向熱收縮率≤0.2%、縱向熱收縮率≤3.6%、橫向拉伸強度≥300MPa、縱向拉伸強度≥200MPa，橫向彈性模量≥4000N/mm2、縱向彈性模量≥2500N/mm2，制得的電容器可在110℃的惡劣環境下長期穩定運行。具體實施方式①供料：取電工級聚丙烯原料，通過真空吸料系統，經金屬檢測器被吸到擠出機上方料斗內，進行自動給料。②擠出塑化：擠出機溫度為210℃～245℃，步驟①中的聚丙烯原料通過擠出機后被加熱熔化，并擠出形成熔融均勻的粘流態熔體。③計量：將步驟②中得出的粘流態熔體經過計量泵后，變成等溫、等壓、等量的熔體進入過濾器。④過濾：采用10微米過濾網對熔體進行過濾，濾去熔體中的雜質及未熔物。⑤模頭定型：模頭各區溫度均設定為245...
【技術保護點】
一種高結晶度雙向拉伸聚丙烯電容膜，其特征是：120℃下靜置15分鐘時的橫向熱收縮率≤0.2%、縱向熱收縮率≤3.6%、橫向拉伸強度≥300MPa、縱向拉伸強度≥200MPa，橫向彈性模量≥4000N/mm
【技術特征摘要】
1.一種高結晶度雙向拉伸聚丙烯電容膜，其特征是：120℃下靜置15分鐘時的橫向熱收縮率≤0.2%、縱向熱收縮率≤3.6%、橫向拉伸強度≥300MPa、縱向拉伸強度≥200MPa，橫向彈性模量≥4000N/mm2、縱向彈性模量≥2500N/mm2。2.一種高結晶度雙向拉伸聚丙烯電容膜的生產方法，其特征包括如下步驟：①供料：采用等規度為98%～99%、灰分含量小于15ppm、熔融指數為2.0g/10min～3.2g/10min的聚丙烯樹脂材料；②熔融擠出:將聚丙烯原料通過擠出機加熱溶化，經模頭形成等溫等壓熔體；③熔體冷卻鑄片成型：將等溫等壓的熔體經冷卻輥冷卻定型，制得厚片；④雙向拉伸：將制得的鑄片通過縱向拉伸機進行預熱、拉伸、定型，制得厚膜；再將厚膜通過橫向拉伸機進行預熱、拉伸、定型，制得薄...
【專利技術屬性】
技術研發人員：徐經樓，陳銀平，陳銀滿，
申請(專利權)人：江蘇中立方實業有限公司，
類型：發明
國別省市：江蘇,32