The invention belongs to the technical field of adhesives, is a kind of high temperature resistant metal adhesives, which consists of the weight of raw materials: 30-40 bauxite, kaolin 10-20, 25-35 phosphate, silicate sol 3-8, aluminum hydroxide 3-6, water 8-12; during the preparation of the aluminum hydroxide mixed with water, adding phosphoric acid, heated under stirring conditions and get the clear liquid, cooling after mixing with bauxite, kaolin, silica sol, stirring into a thick paste, namely; the invention of easily obtained raw materials, simple process, strong adhesion, easy to use, can be used in the condition of high temperature, especially suitable for the repair of heated metal pipes and metal fracture condition the model can be used for boiler pipe grinding cracks or adhesive wear.
【技術實現步驟摘要】
一種耐高溫金屬黏合劑
本專利技術屬于膠粘劑
，具體是一種耐高溫金屬黏合劑。
技術介紹
鍋爐是工業生產中必不可少的設備，鍋爐管道是一種耐高溫、高壓設備，但是由于其長期處于高溫高壓狀態，難免會出現管道磨穿或者裂縫，而一旦發生此類事故，首先要確保生產能夠正常進行，維持到一批產品下線才能進行維修，這樣就需要一種能夠在高溫下進行緊急修補的金屬膠粘劑，以應付突發狀況，保證生產正常進行，而目前普通的膠粘劑都無法在高溫下使用。因此，研發一種高溫專用金屬黏合劑，是鍋爐能夠正常運行的重要保障。
技術實現思路
本專利技術的目的就是針對目前普通的膠粘劑不能在高溫下使用，導致鍋爐管道等在高溫高壓下使用的設備在生產中遇到裂縫或管道磨穿等問題無法及時維修，保障生產正常進行的問題，而提供一種耐高溫金屬黏合劑。本專利技術的一種耐高溫金屬黏合劑,由下述重量份原料組成：高鋁礬土30-40高嶺土10-20磷酸25-35硅酸溶膠3-8氫氧化鋁3-6水8-12；制備時，先將氫氧化鋁與水混合，再加入磷酸，在攪拌狀態下加熱，得到清澈的液體，冷卻后與高鋁礬土、高嶺土、硅酸溶膠混合，攪拌成粘稠膏狀，即得。本專利技術原料易得，工藝簡單，粘接力強，使用方便，凝固后膠不脫落，補漏效果好，可在高溫狀態下使用，尤其適用于修補受熱狀態下的金屬管道及金屬裂縫，可用于鍋爐管道磨穿處或裂縫處的粘合。具體實施方式實施例1本實施例的一種耐高溫金屬黏合劑,由下述重量份原料組成：高鋁礬土25高嶺土15磷酸30硅酸溶膠5氫氧化鋁4水10；制備時，先將氫氧化鋁與水混合，再加入磷酸，在攪拌狀態下加熱，得到清澈的液體，冷卻后與高鋁礬土、高...
【技術保護點】
一種耐高溫金屬黏合劑,其特征在于由下述重量份原料組成：高鋁礬土???????????30?40?????????高嶺土??????????????10?20磷酸???????????????25?35?????????硅酸溶膠????????????3?8氫氧化鋁???????????3?6???????????水??????????????????8?12；制備時，先將氫氧化鋁與水混合，再加入磷酸，在攪拌狀態下加熱，得到清澈的液體，冷卻后與高鋁礬土、高嶺土、硅酸溶膠混合，攪拌成粘稠膏狀，即得。
【技術特征摘要】
1.一種耐高溫金屬黏合劑,其特征在于由下述重量份原料組成：高鋁礬土30-40高嶺土10-20磷酸25-35硅酸溶膠3-8氫氧化鋁3-6水8-1...