The invention relates to a polyvinyl chloride material formulation, which consists of the following raw materials: resin powder 50 70 parts, heavy calcium powder 25 28 parts, calcium stearate 12 15 parts, zinc oxide 2 3 parts, hexamethylphosphatidyl triamide 1 2 parts, paraffin 0.4 0.5 parts, stearic acid 0.3 0.4 parts, polyester wax 0.25 0.3 parts, ethylene bis fatty acid amide 0.5 8 parts, dioctyl ester 0.7 parts. Di-n-octyltin acid 0.5 1 portion. The beneficial effect of the invention is that the addition of hexamethylphosphatidyl triamide can not only greatly improve the antioxidant performance of PVC pipe, but also has high surface finish, and has low ratio, which is suitable for popularization and application.
【技術實現步驟摘要】
聚氯乙烯材料配方
本專利技術涉及材料領域，具體涉及一種聚氯乙烯材料配方。
技術介紹
PVC材料的軟管物美價廉，是目前公認也是應用最多的戶外用水管材料，但現有的PVC軟管材料制成的軟管存在一些缺陷，比如說在戶外長期風吹日曬，老化比較快，目前克服該缺陷的辦法是添加抗氧化劑跟紫外線吸收劑，但添加的物質比較昂貴，致使PVC軟管生產成本較高。
技術實現思路
針對現有技術的不足，本專利技術所要解決的技術問題是，提供一種可以大大提高PVC管材的抗氧化性能，而且成比較低的聚氯乙烯材料配方。本專利技術的具體技術方案如下：一種聚氯乙烯材料配方，由以下重量份數的原料組成：樹脂粉50-70份、重碳鈣粉25-28份、硬脂酸鈣12-15份、氧化鋅2-3份、六甲基磷酰三胺1-2份、石蠟0.4-0.5份、硬脂酸0.3-0.4份、聚酯蠟0.25-0.3份、乙撐雙脂肪酸酰胺0.5-0.8份、二辛脂0.7-1份；馬來酸二正辛基錫0.5-1份。優選的，所述的聚氯乙烯材料配方由以下重量份數的原料組成：樹脂粉60份、重碳鈣粉27份、硬脂酸鈣13份、氧化鋅2份、六甲基磷酰三胺2份、石蠟0.4份、硬脂酸0.4份、聚酯蠟0.25份、乙撐雙脂肪酸酰胺0.6份、二辛脂0.8份；馬來酸二正辛基錫0.8份。本專利技術的有益效果：添加的六甲基磷酰三胺，不但可以大大提高PVC管材的抗氧化性能，表面光潔度高；而且成比較低，適合推廣應用。具體實施方式以下結合具體實施例進一步說明本專利技術。實施例1一種聚氯乙烯材料配方由以下重量份數的原料組成：樹脂粉60份、重碳鈣粉27份、硬脂酸鈣13份、氧化鋅2份、六甲基磷酰三胺2份、石蠟0...
【技術保護點】
1.一種聚氯乙烯材料配方，其特征在于，由以下重量份數的原料組成：樹脂粉50?70份、重碳鈣粉25?28份、硬脂酸鈣12?15份、氧化鋅2?3份、六甲基磷酰三胺1?2份、石蠟0.4?0.5份、硬脂酸0.3?0.4份、聚酯蠟0.25?0.3份、乙撐雙脂肪酸酰胺0.5?0.8份、二辛脂0.7?1份；馬來酸二正辛基錫0.5?1份。
【技術特征摘要】
1.一種聚氯乙烯材料配方，其特征在于，由以下重量份數的原料組成：樹脂粉50-70份、重碳鈣粉25-28份、硬脂酸鈣12-15份、氧化鋅2-3份、六甲基磷酰三胺1-2份、石蠟0.4-0.5份、硬脂酸0.3-0.4份、聚酯蠟0.25-0.3份、乙撐雙脂肪酸酰胺0.5-0.8份、二辛脂0.7-1份；馬來...