The invention discloses a wollastonite fiber preparation method comprises the following steps: A, 990g, CaF210g from natural wollastonite, these raw materials by grinding into 10 mm below the particle; B, the raw material powder into the furnace, heating to 1500-1600 DEG C melting; C, melting in the exit, with silk throwing machine by centrifugation throwing wire; D, silk fibers entered the collector to get wollastonite fiber products. The wollastonite fiber preparation method by melting wollastonite and fused siliceous raw material and limestone with wollastonite blow pull long fiber asbestos use requirements, to completely replace the asbestos fiber wollastonite; tensile strength was 25 x 102MPa - 25 x 102MPa; thermal conductivity under 300 DEG C: 13 14W/m K.
【技術實現(xiàn)步驟摘要】
一種硅灰石纖維制備方法
本專利技術涉及一種制備硅灰石纖維的方法，尤其涉及一種能完全取代石棉的硅灰石纖維制備方法。
技術介紹
石棉纖維對人體有害，許多國家已經禁止使用，現(xiàn)已用天然硅灰石部分替代，但是，由于天然硅灰石的纖維短，限制了它在某些方面的應用，因而不能完全取代石棉。因此，尋找和生產對人體無害、具有較好抗拉強度和較高熱導率的長纖維礦物來完全取代石棉纖維，己經迫在眉睫。
技術實現(xiàn)思路
本專利技術所要解決的技術問題是克服現(xiàn)有技術的缺陷，提供一種硅灰石纖維制備方法，該硅灰石纖維制備方法通過將熔融的硅灰石或熔融的含硅質原料與石灰石吹拉成符合石棉用途要求指標的硅灰石長纖維，達到完全取代石棉的目的；制得的硅灰石長纖維抗拉強度：25x102MPa-25x102MPa；300℃下熱導率：13一14W/m·K。本專利技術解決其技術問題所采用的技術方案是：一種硅灰石纖維制備方法，包括以下步驟：a、稱取天然硅灰石990g、CaF210g，將這些原料通過磨機粉碎成10毫米以下的顆粒；b、將原料粉末投入電阻爐中，加熱至1500-1600℃熔融；c、在熔融出口處，用甩絲機通過離心作用甩成絲；d、成絲得到的纖維進入收集器即得硅灰石纖維成品。進一步的，于原料中添加助熔劑，助熔劑占原料的重量比例為1%一5%，助熔劑為CaF2、B2O3和N2O中的至少一種。進一步的，所述步驟b中熔化時的熔化溫度為1300~1800℃，被投入到電阻爐中時，被粉碎至10毫米以下。綜上所述，本專利技術的一種硅灰石纖維制備方法通過將熔融的硅灰石或熔融的含硅質原料與石灰石吹拉成符合石棉用途要求指標的硅灰石長纖維，達到完...
【技術保護點】
一種硅灰石纖維制備方法，其特征在于，包括以下步驟：a、稱取天然硅灰石990g、CaF210g，將這些原料通過磨機粉碎成10毫米以下的顆粒；b、將原料粉末投入電阻爐中，加熱至1500?1600℃熔融；c、在熔融出口處，用甩絲機通過離心作用甩成絲；d、成絲得到的纖維進入收集器即得硅灰石纖維成品。
【技術特征摘要】
1.一種硅灰石纖維制備方法，其特征在于，包括以下步驟：a、稱取天然硅灰石990g、CaF210g，將這些原料通過磨機粉碎成10毫米以下的顆粒；b、將原料粉末投入電阻爐中，加熱至1500-1600℃熔融；c、在熔融出口處，用甩絲機通過離心作用甩成絲；d、成絲得到的纖維進入收集器即得硅灰石纖維成品。2.根據(jù)權...
【專利技術屬性】
技術研發(fā)人員：李兆源，
申請(專利權)人：江門市蓬江區(qū)億藝廣告設計工作室，
類型：發(fā)明
國別省市：廣東,44
還沒有人留言評論。發(fā)表了對其他瀏覽者有用的留言會獲得科技券。